Dreve FotoDent, Resins for 3D Printers

£169.00£464.50 excl. VAT+Carg.

Dreve FotoDent Accessories for 3D Printers 385nm and 405nm

Clear
Product price
excl. VAT+Carg.
Additional options total:
excl. VAT+Carg.
Order total:
excl. VAT+Carg.
SKU: rshape.fotodent Category:

Dreve Accessories for the Rapidshape 3D Printer by Rapidshape Dental

FotoDent CAST is a light-curing resin for the manufacturing of cauterization profiles for casting technology using 385 or 405 nm-LED-based DLP® systems. For obligatory post curing of FotoDent® cast built parts, the high performance light curing unit FotoDent Flash, PCU Evo and PCU 90 are recommended, which are optimal balanced to the manufacturing process. Properties: Colour: red-transparent, Density: 1.1–1.2 g cm-3, Viscosity: <0.3 Pa s.
Post curing time using PCU LED N2: Asiga 6 min 80% Light Power (Vacuum). Post Curing time using Fotodent Flash: 8 min + 1 min gas pre-flow. Asiga 10 min + 1 min gas pre-flow.
Flexural modulus: >2000 MPa
Flexural strength: >100 MPa
Elongation at break: 7.5–11 %
Hardness: 80–90 Shore D
Cauterisation Residual ash content: ca. 1.5 %
Build speed: Ø 15.3 mm/h

FotoDent® MODEL is a light-curing resin for the manufacturing of dental models using 385405 nm-LED-based DLP® systems. For obligatory post curing of FotoDent® model built parts, the high performance light curing unit FotoDent Flash®, PCU Evo and PCU 90 are recommended, which are optimal balanced to the manufacturing process.
Properties: Colour: opaque beige; Density: 1.1–1.2 g cm-3; Viscosity: 0.8–1.3 Pa s
Post curing time using PCU LED N2: 8 min 80% Light Power (Vacuum). Using Fotodent Flash: 12 min + 1 min gas pre-flow.
Flexural modulus: >1750 MPa; Flexural strength: >85 MPa; Elongation at break: 11–15 %;
Hardness: 80–85 Shore D

FotoDent® MODEL-2 is a light-curing resin for the manufacturing of dental models using new generation printers 385 nm-LED-based DLP® systems. Light-curing resin for the manufacturing of dental models for orthodontics and prothetics. Faster printing process because of higher output with accustomed precision.
Properties: Colour: opaque beige; Density: 1.1–1.2 g cm-3; Viscosity: 1.0–0.2 Pa s
Post curing time using PCU LED N2 & Asiga: 8 min 80% Light Power (Vacuum). Using Fotodent Flash: 8 min + 1 min gas pre-flow. Asiga: 12 min + 1 min gas pre-flow
Flexural modulus: >1900 MPa; Flexural strength: >85 MPa; Elongation at break: 11–15 %;
Hardness: 80–85 Shore D

FotoDent® Guide is a light-curing resin for the manufacturing of dental models using 385 or 405 nm-LED-based DLP® systems. For obligatory post curing of FotoDent® model built parts, the high performance light curing unit FotoDent Flash®, PCU Evo and PCU 90 are recommended, which are optimal balanced to the manufacturing process.
Properties: Colour: Blue transparent; Density: 1.1–1.2 g cm-3; Viscosity: 0.6–1.05 Pa s
Post curing time using PCU LED N2: 5 min 33% Light Power. Using Fotodent Flash: 6 min + 1 min gas pre-flow. Post Curing 405nm: 10 min + 1 min gas pre-flow
Flexural modulus: >1700 MPa; Flexural strength: >75 MPa; Elongation at break: 10–15 %;
Hardness: 80–85 Shore D

FotoDent® GINGIVA is a light-curing resin for the manufacturing of dental gingiva-models using 385 nm-LED-based DLP® systems. For obligatory post curing of FotoDent® gingiva built parts, the high performance light curing unit FotoDent Flash®, PCU Evo and PCU 90 are recommended, which are optimal balanced to the manufacturing process.
Properties; Colour: pink; Density: 1.1–1.3 g cm-3; Viscosity: 1.1–1.5 Pa s
Post curing time Fotodent Flash: 10 min + 1 min gas pre-flow. PCU LED: 8 min 80% Light Power.
Tensile strength: >20 MPa; Tensile elongation: >100 %; Tear resistance: ≥ 15 N mm-1;
Hardness (23 °C): ca. 70 Shore D

FotoDent® TRAY is a light-curing resin for the manufacturing of dental impression trays using 385-405 nm-LED-based DLP® systems. Biocompatible light-curing resin for the manufacturing of dental impression trays. High reactivity at low viscosity. The finished impression trays have a homogeneous surface, which significantly reduces manual reworking. Properties; Colour: Green; Density: 1.1 g cm-3

Post Curing: Using Fotodent Flash: 10 min + 1 min gas pre-flow. PCU LED N2: 10 min 80% Light Power. For D90 II Fotodent Flash 12 min + 1 min gas pre-flow.

NEW Dreve Fotodent Setup using 385-405 nm-LED-based DLP® systems

Light-curing resin for the production of orthodontic set-up models. The material is above all characterised by its increased building speed. The set-up models are very well suitable for the thermoforming technique.

MaizeProperties: Colour: Colour: Golden Maize; Density: 0.9–1.0g cm-3; Viscosity: 1.0–1.5 Pa s

Flexural modulus: >2000 MPa; Flexural strength: >95 MPa; Elongation at break: 5 %;
Hardness: 80–85 Shore D

Post Curing: PCU LED N2: 10 min 80% Light Power. Fotodent Flash and PCU Evo:  8 min + 1 min gas pre-flow.

Additional information

Audience

,

Manufacturer

,

Type/QTY

Model (405nm printers) 1Kg, Model 2 (385nm printers) 1Kg, Cast 1kg, Guide 385nm printers 1kg, Guide 405nm printers 1kg, Tray 1kg, Gingiva 385nm 1Kg, FotoDent Setup 385nm/405nm (Maize Yellow) 1Kg

Reviews

There are no reviews yet.

Only logged in customers who have purchased this product may leave a review.