InCoris TZI C, medi S L40x W19x H15.5mm
The blocks are initially manufactured in a partially sintered state; then, enlarged by the inLab CAD/CAM system, they are individually processed to specification, and finally, densely sintered.
The aesthetic features of inCoris TZI C enable application as fully anatomical crowns and bridges.
The advantages of inCoris TZI C include:
Resistance to corrosion
Good biological compatibility of the product
5 pre-dyed classical shades, A1 – A4
The following specifications apply to material that is densely sintered in an inFire HTC / inFire HTC speed sintering furnace.
Density 6.08 g cm-3
Fracture toughness KIC 6.4 MPa m1/2
Thermal expansion coefficient (20 – 500 °C): 11 10-6 K-1
Bending strength: > 900 MPa